Face Pads Design
The face pad is assembled with a flat pad and a corner pad as shown in the figure.
Specifications
| Types | Dimension ( L x W mm) ( thickness is 30mm or 40mm ) | |||||
|---|---|---|---|---|---|---|
| Flat Pad | 500 x 500 | 600 x 600 | 600 x 450 | 600 x 300 | 450 x 450 | 300 x 300 |
| Corner Pad | 500 x 220 | 600 x 220 | 300 x 220 | 450 x 220 | 380 x 220 | |
- Types
- Flat Pad
- Dimension ( L x W mm) ( thickness is 30mm or 40mm )
- 500 x 500
- 600 x 600
- 600 x 450
- 600 x 300
- 450 x 450
- 300 x 300
- Types
- Corner Pad
- Dimension ( L x W mm) ( thickness is 30mm or 40mm )
- 500 x 220
- 600 x 220
- 300 x 220
- 450 x 220
- 380 x 220
Material
Ultra high molecular weight polyethylene or Nylon resin are chosen as the material for face pads whose performances are shown in the following table.
Physical Performance
| Physical performance/ Material | Density | Elongation at Break %≥ | Tensile Strength MPa≥ | Abrision Rate | Friction Factor | Yield Strength MPa≥ | Compression Strength MPa≥ | Resistance of shocks Kg/cm | Youngs Mudulus Kg/cm² |
|---|---|---|---|---|---|---|---|---|---|
| Nylon Resin | 1.15 | 20 | 68.6 | 0.3 | 0.2 | 98 | 88.2 | 200 | 200 |
| PE Resin | 0.9-1.00 | 20 | 24.5 | 0.5 | 0.2 | 19.6 | 19.6 | 75 | 5600-10500 |
- Physical performance/ Material
- Nylon Resin
- Physical performance/ Material
- Density
- Elongation at Break %≥
- Tensile Strength MPa≥
- Abrision Rate
- Friction Factor
- Yield Strength MPa≥
- Compression Strength MPa≥
- Resistance of shocks Kg/cm
- Youngs Mudulus Kg/cm²
- Nylon Resin
- 1.15
- 20
- 68.6
- 0.3
- 0.2
- 98
- 88.2
- 200
- 200
- Physical performance/ Material
- PE Resin
- Physical performance/ Material
- Density
- Elongation at Break %≥
- Tensile Strength MPa≥
- Abrision Rate
- Friction Factor
- Yield Strength MPa≥
- Compression Strength MPa≥
- Resistance of shocks Kg/cm
- Youngs Mudulus Kg/cm²
- PE Resin
- 0.9-1.00
- 20
- 24.5
- 0.5
- 0.2
- 19.6
- 19.6
- 75
- 5600-10500