Rubber Property

GLEN’s rubber fenders are manufactured from the highly quality nature rubber and other styrene butadiene SBR based compounds to satisfy various performance requirements. Other special rubber is also available upon customers’ special requirements. The main performance index are shown as below: 

Property Testing Standard Unit Value
 Tensile strength  GB/T 528,1;ASTM D 412 Die C; ISO 37; DIN53504; AS1180.2; BS 903.A2; JISK6251  MPa  ≥16t
 Elongation at break  GB/T 528,1;ASTM D 412 Die C; ISO 37; DIN53504; AS1180.2; BS 903.A2; JISK6251 %  ≥300
 Compression set (70℃, 22h,25%)  GB/T7759,1;ASTM D395 ISO815; DIN53517; AS1683.15.2B; BS 903.A3; JISK6262 %  ≤30
 Hardness ( shore A)  GB/T531,1;ASTM D2240 ISO815; DIN53505; AS1683.15.2B; BS 903.A26; JISK6253  Degree  ≤84
 Tear resistance Die B  GB/T529; Crescent Test Piece; ASTM624 ISO34.1; DIN53507; AS1683.12; BS 903.A 3; JISK6253  N/mm  ≥70
 Ozone resistance (40℃,48h,20%,50pphm)  GB/T13642;ASTM D1149 ISO34.1; DIN53509; AS1683.24; BS 903.A 43; JISK6259   No cracking
Hot air aging (70℃, 96h)  Variation ratio of tensile strength  GB/T13512;ASTM D412 Die C; ISO37; DIN53504; AS1180.2; BS 903 A 19; JISK6257 %  
Variation ratio of Elongation at break GB/T13512;ASTM D412 Die C; ISO37; DIN53504; AS1180.2; BS 903 A 19; JISK6257 %  
 Hardness ( shore A)  GB/T531;ASTM D412 Die C; ISO815; DIN53505; AS1683.15.2B; BS 903 A 26; JISK6253  degree  Max +8

rubberfender_rubberproperty_03b

rubberfender_rubberproperty_06c

See More

News

24 October 2017
KORMARINE 2017 held from October 24th to 27th,2017 in Busan,Korea

KORMARINE 2017 is the top trade exhibition in the Asia Pacific region. The Asian market is the most important target for those who want to expand their world business.

13 November 2017
The 20th Middle East (Abu Dhabi) International Petroleum Products Exhibition (ADIPEC 2017)

The 20th Middle East (Abu Dhabi) International Petroleum Products Exhibition (ADIPEC 2017) will be held from November 13 to November 16, 2017 at the United Arab Emirates - Abu Dhabi National Exhibition Center!